Aromatization catalyst comprising prolongated silica and methods of making and using same

ABSTRACT

A prolongated silica bound zeolite support comprising from about 85 wt % to about 95 wt % zeolite. A catalyst composition comprising a prolongated silica bound zeolite supporting at least one Group VIII metal and at least one halide. A process of making a prolongated silica bound zeolite support comprising mixing a zeolite, a prolongated silica, and water to form a mixture, and shaping the mixture into the prolongated silica bound zeolite support. A process of making a prolongated silica bound zeolite catalyst comprising mixing a zeolite, a prolongated silica, and water to form a mixture, shaping the mixture into a prolongated silica bound zeolite support, and adding one or more catalytic compounds to the prolongated silica bound zeolite support to form the prolongated silica bound zeolite catalyst. A process for converting hydrocarbons to aromatics comprising: contacting a prolongated silica bound zeolite catalyst comprising at least one Group VIII metal and at least one halide with a hydrocarbon feed in a reaction zone under aromatization conditions; recovering an aromatic product from the reaction zone; and purifying the aromatic product to produce benzene, toluene, paraxylene, orthoxylene, metaxylene, or combinations thereof.

FIELD OF THE INVENTION

The present disclosure relates to catalyst compositions. Morespecifically, the present disclosure relates to improved aromatizationcatalyst compositions and methods of producing same.

BACKGROUND OF THE INVENTION

Large pore zeolite catalysts are useful to dehydrocyclize aliphatichydrocarbons to produce aromatic hydrocarbons. For example, large porezeolite catalysts are useful for reforming light petroleum naphtha (e.g.C₆-C₈) to benzene, toluene and xylenes. Examples of such aromatizationcatalysts include silica bound large pore zeolite supports containingplatinum and halides such as chloride and fluoride. Due to thecommercial importance of such catalysts, an ongoing need exists forimproved aromatization catalysts and methods of making and using same.

SUMMARY OF THE INVENTION

Disclosed herein is a prolongated silica bound zeolite supportcomprising from about 50 wt % to about 95 wt % zeolite.

Also disclosed herein is a catalyst composition comprising a prolongatedsilica bound zeolite supporting at least one Group VIII metal and atleast one halide.

Further disclosed herein is a process of making a prolongated silicabound zeolite support comprising mixing a zeolite, a prolongated silica,and water to form a mixture, and shaping the mixture into theprolongated silica bound zeolite support.

Further disclosed herein is a process of making a prolongated silicabound zeolite catalyst comprising mixing a zeolite, a prolongatedsilica, and water to form a mixture, shaping the mixture into aprolongated silica bound zeolite support, and adding one or morecatalytic compounds to the prolongated silica bound zeolite support toform the prolongated silica bound zeolite catalyst.

Further disclosed herein is a process for converting hydrocarbons toaromatics comprising: contacting a prolongated silica bound zeolitecatalyst comprising at least one Group VIII metal and at least onehalide with a hydrocarbon feed in a reaction zone under aromatizationconditions; recovering an aromatic product from the reaction zone; andpurifying the aromatic product to produce benzene, toluene, paraxylene,orthoxylene, metaxylene, or combinations thereof.

The foregoing has outlined rather broadly the features and technicaladvantages of the present disclosure in order that the detaileddescription that follows may be better understood. Additional featuresand advantages of the embodiments will be described hereinafter thatform the subject of the claims of the disclosure. It should beappreciated by those skilled in the art that the conception and thespecific embodiments disclosed may be readily utilized as a basis formodifying or designing other structures for carrying out the samepurposes of the present disclosure. It should also be realized by thoseskilled in the art that such equivalent constructions do not depart fromthe spirit and scope of the embodiments of the disclosure as set forthin the appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

For a detailed description of the embodiments of the apparatus andmethods of the present disclosure, reference will now be made to theaccompanying drawing in which:

FIG. 1 is a drawing of a prolate spheroid.

DETAILED DESCRIPTION

Disclosed herein are prolongated silica bound zeolite supports,prolongated silica bound zeolite catalysts, and methods of making andusing same. The prolongated silica bound zeolite support may be preparedby blending a zeolite, a prolongated silica, and water to form a mixtureand shaping the mixture into the silica bound zeolite support, which isreferred to herein as the catalyst base or catalyst support. Theprolongated silica bound zeolite catalysts may be prepared by contactingthe prolongated silica bound zeolite support with one or more catalyticcompounds such as a Group VIII metal (e.g., platinum) and one or morehalides (e.g., chloride and fluoride). The prolongated silica boundzeolite catalysts may be used as catalysts in reforming processes suchas for example, the conversion of hydrocarbons to aromatics, and may becollectively termed aromatization catalyst compositions. The prolongatedsilica bound zeolite catalyst compositions disclosed herein may becharacterized by an increased concentration of active catalyticmaterial, a reduced temperature start of reaction (TSOR), or both whencompared to an otherwise identical composition lacking a prolongatedsilica.

The prolongated silica bound zeolite support comprises one or morezeolites that are bound together by a binder material. The term“zeolite” generally refers to hydrated, crystalline metalaluminosilicates. These zeolites exhibit a network of SiO₄ and AlO₄tetrahedra in which aluminum and silicon atoms are crosslinked in athree-dimensional framework by sharing oxygen atoms. In the framework,the ratio of oxygen atoms to the total of aluminum and silicon atoms isequal to 2. The framework exhibits a negative electrovalence thattypically is balanced by the inclusion of cations within the crystalsuch as metals, alkali metals, alkaline earth metals, or hydrogen. Thus,zeolites are a group of natural or synthetic hydrated aluminosilicateminerals that contain alkali and alkaline metals. Zeolites arecharacterized by a framework structure that encloses interconnectedcavities occupied by ion-exchangeable large metal cations such aspotassium and water molecules permitting reversible dehydration. Theactual formula of the zeolite may vary without changing the crystallinestructure. In an embodiment, the mole ratio of silicon to aluminum(Si/Al) in the zeolite may vary from about 1.0 to about 3.5.

In an embodiment, the catalyst support comprises a large-pore zeolite.The term “large-pore zeolite” as used herein refers to a zeolite havingan effective pore diameter of from about 6 Angstroms (Å) to about 15 Å,alternatively from about 7 Å to about 9 Å. Large pore crystallinezeolites suitable for use in this disclosure include without limitationL-zeolite, X-zeolite, Y-zeolite, omega zeolite, beta zeolite, ZSM-4,ZSM-5, ZSM-10, ZSM-12, ZSM-20, REY, USY, RE-USY, LZ-210, LZ-20-A,LZ-20-M, LZ-20-T, SSZ-24, ZZA-26, SSZ-31, SSZ-33, SSZ-35, SSZ-37,SSZ-41, SSZ-42, SSZ-44, MCM-58, mordenite, faujasite, or combinationsthereof. In an embodiment, the large pore zeolite has an isotypicframework structure. In an embodiment, the catalyst support comprisesL-zeolite.

L-type zeolites are a sub-group of zeolites. The designations LTLzeolite or Linde type L zeolite also refer to this same sub-group ofzeolitic catalysts. Typical L-type zeolites contain mole ratios ofoxides in accordance with the following formula:M._(2/n)O.Al.₂O₃ .xSiO₂ .yH₂Owherein “M” designates at least one exchangeable cation such as barium,calcium, cerium, lithium, magnesium, potassium, sodium, strontium, andzinc as well as non-metallic cations like hydronium and ammonium ionswhich may be replaced by other exchangeable cations without causing asubstantial alteration of the basic crystal structure of the L-typezeolite. The “n” in the formula represents the valence of “M”, “x” is 2or greater; and “y” is the number of water molecules contained in thechannels or interconnected voids with the zeolite. L-zeolite, its X-raydiffraction pattern, its properties, and methods for its preparation aredescribed in detail in U.S. Pat. No. 3,216,789, the content of which ishereby incorporated by reference. In an embodiment, the catalyst supportcomprises L-zeolite wherein M is potassium, also referred to asKL-zeolite.

The catalyst support further comprises a binder. In an embodiment, thebinder comprises a prolongated silica, alternatively a low acidityprolongated silica. FIG. 1 illustrates an embodiment of a prolongatedsilica, 100. Embodiments of the prolongated silica are characterizedgenerally by a prolated spheroid or ellipsoid shape also termedcigar-shaped, watermelon-shaped, rice-shaped, spindle-shaped orfootball-shaped. As defined herein a prolate spheroid is a quadricsurface in three dimensions obtained by rotating an ellipse about one ofits principal axes having a polar diameter longer than its equatorialdiameter where a and b are the equatorial radii and c is the polarradius. In a prolate spheroid or ellipsoid a is equal to b but a and bare both less than c. When viewed as a transverse cross section, a isthe semi-minor axis, and c is the semi-major axis where c is greaterthan a in an ellipse. The aspect ratio, as defined herein m is the ratioof c to a.

In an embodiment, the prolongated silica comprises particles having adiameter of from about 5 nm to about 20 nm, alternatively from about 8nm to about 16 nm and a length of from about 30 nm to about 400 nm,alternatively from about 35 nm to about 350 nm. In an embodiment, theprolongated silica particles may be in the form of a silica sol. Asilica sol may be obtained by dispersing the silica particles in water.The silica sol may be provided in about 20 to about 30 vol % aqueoussolution having a pH of from about 9.0 to about 10.5 with a viscosity ofequal to or less than about 20 mPa·s at 25° C., alternatively from about1 to about 20 mPa·s at 25° C. An example of a silica sol suitable foruse in this disclosure includes without limitation SNOWTEX® UP which isa colloidal silica sol comprising prolongated silica particles that iscommercially available from Nissan Chemical Industries Ltd. The bindermay additionally comprise synthetic or naturally occurring zeolites;alumina; clays such as montmorillonite and kaolin; the refractory oxidesof metals of Groups IVA and IVB of the Periodic Table of the Elements;oxides of silicon, titanium, zirconium or combinations thereof; orcombinations thereof.

In an embodiment, the prolongated silica bound zeolite support may beprepared by forming a mixture comprising a zeolite, a prolongatedsilica, water and optional extrusion aids and then shaped. The mixturemay be formed into a suitable shape, for example via extrusion. Themixture may contain from about 85 wt. % to about 95 wt. % zeolite,alternatively from about 75 wt. % to about 90 wt. % zeolite,alternatively from about 50 wt. % to about 95 wt. % zeolite. The mixturemay contain zeolite and a prolongated silica binder combined in a weightratio of from about 1:99 to about 99:1, alternatively from about 90:10to about 85:15, alternatively from about 92:8 to about 82:18. In anembodiment, the aqueous volume percent of the mixture formed bycombining the zeolite and binder (e.g., prolongated silica) may be fromabout 20% to about 60%, alternatively from about 25% to about 55%,alternatively from about 30% to about 45%. In an embodiment, the mixturewill contain sufficient water to retain a desired shape. Water may beadded separately to the mixture or as a solution of one or more othercomponents, for example silica sol. The amount of water required toretain a desired shape of the shaped mixture may be varied and selectedaccording to ordinary skill in the art. In an embodiment, the mixture isextruded and may contain up to about 50 grams of water per about 100grams of extrudate.

In an embodiment, the mixture comprises L-zeolite bound with aprolongated silica, alternatively L-zeolite bound with a prolongated,colloidal silica, alternatively KL-zeolite bound with a prolongatedsilica, alternatively KL-zeolite bound with a prolongated, colloidalsilica.

In an embodiment, the mixture comprising a silica bound zeolite isformed into shaped particles. In an embodiment, the mixture may beformed into any suitable shape. Methods for shaping particles are wellknown in the art, and include, for example, extrusion, spray drying,pelletizing, agglomerization and the like. In an embodiment, the mixtureis formed into an extrudate, for example as described in U.S. Pat. Nos.5,558,851 and 5,514,362 each of which are incorporated herein in theirentirety. In an embodiment, the mixture further comprises an extrusionaid. An extrusion aid may function to improve the rheology of themixture. This improvement in the rheology of the mixture may function toimprove flow of the mixture through the extrusion die. Improved flowthrough the extrusion die leads to easier equipment start-up, smootherextrusion, faster processing, lower extrusion pressures, and improvedproduct appearance. In an embodiment, the extrusion aid may comprisecellulose derivatives, ethylene glycol, stearic acid or combinationsthereof. In an embodiment, the extrusion aid comprises a cellulose ethersuch as methylcellulose, carboxymethylcellulose,ethylhydroxyethylcellulose, hydroxyethylcellulose,hydroxypropylcellulose, methylhydroxyethylcellulose,methylhydroxypropylcellulose, or combinations thereof. An example of anextrusion aid suitable for use in this disclosure includes withoutlimitation METHOCEL®, a cellulose based material commercially availablefrom Dow Chemical Company. Extrusion aids, their effective amounts andmethods of incorporation into mixture may be varied and selectedaccording to ordinary skill in the art. Hereafter the shaped mixtureexiting a die will be referred to as the “green extrudate.”

Excess water from the green extrudate may be removed by drying to form adried green extrudate prior to further processing. Conventional methodsfor drying wet solids can be used to dry the green extrudate, and mayinclude, for example drying in air or an inert gas such as nitrogen orhelium. The air or inert gas may be circulating, moving, or static.Drying temperatures may range from about 200° F. to about 400° F.,alternatively from about 200° F. to about 300° F., alternatively fromabout 225° F. to about 275° F. Drying times may range from equal to orgreater than about 1 hour, alternatively from about 1 hour to about 10hours, alternatively from about 2 hours to about 5 hours.

In an embodiment, the dried green extrudate may be calcined to form acalcined extruded base (CEB). Calcination temperatures may range fromabout 500° F. to about 1500° F., alternatively from about 700° F. toabout 1100° F., alternatively from about 850° F. to about 1100° F.Calcination times may range from about 0.5 to about 5 hours,alternatively from about 0.5 to about 1.5 hours. In such embodiments,the calcination may be carried out in an oxygen containing atmospherehaving an air flow of from about 10 to about 20 cubic feet per hour(CFH), alternatively the calcination may be carried out in air at a flowof from about 10 to about 20 CFH, alternatively, the calcination may becarried out in “dry” air having an air flow of about 10 to about 20 CFH.As used herein “dry” air refers to air having a dew point of less thanabout −40° F. The calcined extruded base is a prolongated silica boundzeolite support and may be directly used in a catalyst preparation, seebelow, or may be further processed according to the followingdescription.

In an embodiment, the CEB may be washed to form a washed CEB. While notwishing to be bound by any one theory, it is believed that washing theCEB may reduce the amount of “readily removable” alkali present. Theterm washing, as used herein, is meant to include any process whereliquid (e.g. water) in excess of the material's pore volume is contactedwith the CEB. The “readily removable” alkali is defined herein as thealkali that can be washed out of the CEB after 1, 2, 3, 4, or 5 washings(1:1 volume of liquid to wt of extrudate) at ambient temperature. In anembodiment, the wash water is distilled or deionized water having a pHof from about 5 to about 9. The washing temperature may range from about70° F. to about 200° F., alternatively of from about 80° F. to about130° F., alternatively from about 90° F. to about 110° F. The washingtime may range from about 5 to about 60 minutes per wash, alternativelyfrom about 15 to about 30 minutes per wash.

After washing to reduce the amount of readily removable alkali, thewashed CEB may be dried to form a washed and dried CEB. The dryingtemperature may range from about 200° F. to about 400° F., alternativelyfrom about 200° F. to about 300° F., alternatively from about 225° F. toabout 275° F. The drying time may range from at least about 1 hour,alternatively from about 1 to about 10 hours, alternatively from about 2to about 5 hours.

The washed and dried CEB may be recalcined to form a washed, dried, andrecalcined CEB. The calcining temperature may range from about 500° F.to about 1200° F., alternatively from about 700° F. to about 1100° F.,alternatively from about 850° F. to about 1000° F. The calcining timemay range from about 0.5 to about 5.0 hours, alternatively from about0.5 to about 1.5 hours. In such embodiments, the calcination may becarried out in an oxygen containing atmosphere having an air flow offrom about 10 to about 20 CFH, alternatively the calcination may becarried out in air at a flow of from about 10 to about 20 CFH,alternatively, the calcination may be carried out in “dry” air having anair flow of about 10 to about 20 CFH. The washed, dried, and recalcinedCEB is a prolongated silica bound zeolite support and may be directlyused in a catalyst preparation as described herein.

The prolongated silica bound zeolite support having been processed aspreviously disclosed herein may be further processed to add one or morecatalytic compounds to the support. In an embodiment, the addition of ametal and one or more halides to the support forms an aromatizationcatalyst capable of catalyzing the conversion of hydrocarbons toaromatics.

In an embodiment, the prolongated silica bound zeolite support isimpregnated with one or more Group VIII metals to form a metalizedprolongated silica bound zeolite support. The metal may be added to thesupport by employing a variety of known and conventional techniques,e.g., ion-exchange, incipient wetness, pore fill, impregnation, etc. Inan embodiment, the metal is added to the support by impregnation with ametal-containing solution. The metal in the metal containing solutionmay be at least one Group VIII metal; alternatively, Pt, Pd, Rh, Ir, Ru,Os, or combinations thereof; alternatively, platinum. In an embodiment,the metal comprises platinum that is added to the support via contactwith a metal-containing solution containing at least oneplatinum-containing compound. Examples of suitable platinum-containingcompounds for contact with the support include without limitationplatinum compounds that form positively charged platinum complex ions insolution such as for example platinum salts such as chlorides andnitrates; platinum complexes with ammines; or combinations thereof. Forexample, the platinum-containing compound can be any platinum-containingcompound including, but not limited to, ammonium tetrachloroplatinate,chloroplatinic acid, diammineplatinum (II) nitrite,bis-(ethylenediamine)platinum (II) chloride, platinum (II)acetylacetonate, dichlorodiammine platinum, platinum (II) chloride,tetraammineplatinum (II) hydroxide, tetraammineplatinum chloride,tetraammineplatinum (II) nitrate, or combinations thereof. In anembodiment, the platinum source is tetraammine platinum chloride (TAPC).The amount of platinum in the metalized support may range from about 0.1to about 5 wt. %, alternatively from about 0.1 to about 3 wt. %,alternatively from about 0.3 to about 1.8 wt. %.

In an embodiment, one or more halides are added to the prolongatedsilica bound zeolite support by contact with a halide-containingcompound to form a halided support. The halides may be added to thesupport separately; alternatively, the halides may be added to thesupport at the same time. Such halides may be incorporated during thepreviously described metallization, alternatively the halides may beincorporated during a separate step that may be pre- or post addition ofthe metal, to form a metalized and halided prolongated silica boundzeolite support. Examples of suitable halides include without limitationfluoride, chloride, bromide, iodide, or combinations thereof. Suchhalides may be introduced as an organic ammonium halide compound. Theorganic ammonium halide compound may comprise one or more compoundsrepresented by the formula N(R)₄X, where X is a halide and where Rrepresents a hydrogen or a substituted or unsubstituted carbon chainmolecule having 1-20 carbons wherein each R may be the same ordifferent. In an embodiment, R is selected from the group consisting ofmethyl, ethyl, propyl, butyl, and combinations thereof, morespecifically methyl. Examples of suitable organic ammonium compoundsrepresented by the formula N(R)₄X include ammonium chloride, ammoniumfluoride, and tetraalkylammonium halides such as tetramethylammoniumchloride (TMAC), tetramethylammonium fluoride (TMAF), tetraethylammoniumchloride, tetraethylammonium fluoride, tetrapropylammonium chloride,tetrapropylammonium fluoride, tetrabutylammonium chloride,tetrabutylammonium fluoride, methyltriethylammonium chloride,methyltriethylammonium fluoride, or combinations thereof. In anembodiment, the halided prolongated silica bound zeolite supportcomprises chloride present in an amount of from about 0.1 to about 5 wt.%, alternatively from about 0.1 to about 3 wt. %, alternatively fromabout 0.3 to about 1.8 wt. %. In an embodiment, the halided prolongatedsilica bound zeolite support comprises fluoride present in an amount offrom about 0.1 to about 5 wt. %, alternatively from about 0.1 to about 3wt. %, alternatively from about 0.3 to about 1.8 wt. %. In anembodiment, the halided prolongated silica bound zeolite supportcomprises both chloride and fluoride, which may be present in a Cl:Fratio of from about 1:10 to about 10:1, alternatively from about 1:5 toabout 5:1 alternatively from about 1:2 to about 2:1. Once the supporthas been contacted with halogens and metal it is hereinafter referred toas a halided, metallized support (HMS). In an embodiment, the HMS isallowed to set for several hours prior to additional processing. In anembodiment, the HMS is allowed to set for about 1 to about 24 hours,alternatively for about 2 to about 8 hours, alternatively for about 3 toabout 6 hours.

Following the preparation of the HMS by contact with a metal and one ormore halides the HMS may then be further processed as described herein.The HMS may be processed to remove undesirable compounds remaining fromthe contacting steps, for example by drying to remove compounds and/orheating to decompose compounds. In an embodiment, the loaded support isdried, and calcined as described previously.

The HMS may be dried to form a dried HMS, which is an aromatizationcatalyst. The drying temperature may range from about 100° F. to about300° F., alternatively from about 150° F. to about 250° F.,alternatively from about 200° F. to about 220° F. The drying time mayrange from about 0.1 to about 6 hours, alternatively from about 0.2 toabout 4 hours, alternatively from about 0.2 to about 3 hours. The HMSmay be dried using any equipment known to one of ordinary skill in theart for drying under the disclosed conditions. For example, the HMS maybe dried using a standard rotary evaporator operating at greater thanabout 100° F. and under a pressure of about 20 to about 30 inches ofmercury.

The dried HMS may be calcined to form a dried and calcined HMS, which isan aromatization catalyst. The calcining temperature may range fromabout 400° F. to about 900° F., alternatively from about 500° F. toabout 700° F., alternatively from about 550° F. to about 600° F. Thecalcining time may range from about 0.5 to about 5 hours, alternativelyfrom about 0.5 to about 2.5 hours. The calcination may be carried out inan oxygen containing atmosphere under a gas flow rate of from about 5 toabout 20 CFH. Alternatively, the calcination may be carried out in airusing a flow rate of from about 5 to about 20 CFH, alternatively in dryair using a flow rate of about 5 to about 20 CFH. Upon completion ofprocessing the dried, and calcined HMS may be employed as anaromatization catalyst in a suitable chemical reaction and process.

In an embodiment, the HMS prepared as disclosed herein is used as acatalyst in an aromatization reactor system comprising at least onearomatization reactor and its corresponding processing equipment andwill be referred to hereafter as a aromatization catalyst or catalyst.As used herein, the terms “aromatization,” “aromatizing” and “reforming”refer to the treatment of a hydrocarbon feed to provide an aromaticsenriched product, which in one embodiment is a product whose aromaticscontent is greater than that of the feed. Typically, one or morecomponents of the feed undergo one or more reforming reactions toproduce aromatics. Some of the hydrocarbon reactions that occur duringthe aromatization operation include the dehydrogenation of cyclohexanesto aromatics, dehydroisomerization of alkylcyclopentanes to aromatics,dehydrocyclization of acyclic hydrocarbons to aromatics, or combinationsthereof. A number of other reactions also occur, including thedealkylation of alkylbenzenes, isomerization of paraffins, hydrocrackingreactions that produce light gaseous hydrocarbons, e.g., methane,ethane, propane and butane, or combinations thereof.

The aromatization reaction occurs under process conditions thatthermodynamically favor the dehydrocyclization reaction and limitundesirable hydrocracking reactions. The pressures may be from about 0pounds per square inch gauge (psig) to about 500 psig, alternativelyfrom about 25 psig to about 300 psig. The molar ratio of hydrogen tohydrocarbons may be from about 0.1:1 to about 20:1, alternatively fromabout 0.5:1 to about 6:1. The operating temperatures include reactorinlet temperatures from about 700° F. to about 1050° F., alternativelyfrom about 900° F. to about 1025° F. Finally, the liquid hourly spacevelocity for the hydrocarbon feed over the aromatization catalyst may befrom about 0.1 to about 10, alternatively from about 0.5 to about 2.5.

The composition of the feed is a consideration when designing catalyticaromatization systems. In an embodiment, the hydrocarbon feed comprisesnon-aromatic hydrocarbons containing at least six carbon atoms. The feedto the aromatization system is a mixture of hydrocarbons comprising C₆to C₈ hydrocarbons containing up to about 10 wt % and alternatively upto about 15 wt % of C₅ and lighter hydrocarbons (C₅ ⁻) and containing upto about 10 wt % of C₉ and heavier hydrocarbons (C₉ ⁺). Such low levelsof C₉+ and C₅ ⁻ hydrocarbons maximize the yield of high value aromatics.In some embodiments, an optimal hydrocarbon feed maximizes thepercentage of C₆ hydrocarbons. Such a feed can be achieved by separatinga hydrocarbon feedstock such as a full range naphtha into a lighthydrocarbon feed fraction and a heavy hydrocarbon feed fraction, andusing the light fraction.

In another embodiment, the feed is a naphtha feed. The naphtha feed maybe a light hydrocarbon, with a boiling range of about 70° F. to about450° F. The naphtha feed may contain aliphatic, naphthenic or paraffinichydrocarbons. These aliphatic and naphthenic hydrocarbons are converted,at least in part, to aromatics in the aromatization reactor system.While catalytic aromatization typically refers to the conversion ofnaphtha, other feedstocks can be treated as well to provide an aromaticsenriched product. Therefore, while the conversion of naphtha is oneembodiment, the present disclosure can be useful for activatingcatalysts for the conversion or aromatization of a variety of feedstockssuch as paraffinic hydrocarbons, olefinic hydrocarbons, acetylenichydrocarbons, cyclic paraffin hydrocarbons, cyclic olefin hydrocarbons,and mixtures thereof, and particularly saturated hydrocarbons.

Preferably, the feedstock is substantially free of sulfur, nitrogen,metals, and other known poisons for aromatization catalysts. In anembodiment, the feedstock contains less than about 100 ppb of sulfur. Ifpresent, such poisons can be removed using methods known to thoseskilled in the art. In some embodiments, the feed can be purified byfirst using conventional hydrofining techniques, then using sorbents toremove the remaining poisons. Such hydrofining techniques and sorbentsare included in the purification process described below.

In an embodiment, the aromatization catalyst may be used for theproduction of an aromatic product which may then be recovered from thereaction zone and processed subsequently to produce benzene, toluene,paraxylene, orthozylene, metaxylene or combinations thereof. Forexample, the aromatization catalyst may be used in a process comprisingaromatizing a wide boiling range naphtha in a reformer, for example, acontinuous catalytic reformer or semi-regenerative reformer, followed bydistillation of the reformer effluent into an aromatics fraction. Thearomatics fraction may comprise benzene, toluene, paraxylene,orthozylene, metaxylene or combinations thereof.

The xylene isomers orthoxylene, metaxylene, and paraxylene, areimportant chemical intermediates. Orthoxylene may be oxidized to makephthalic anhydride, which is used to make phthalate-based plasticizersamong other things. Metaxylene may be oxidized to make isophthalic acid,which is used in unsaturated polyester resins. Paraxylene may beoxidized to make terephthalic acid, which in turn is used to makepolymers such as polytrimethyleneterephthalate,polybutyleneterephthalate (PBT), and polyethyleneterephthalate (PET).PET is one of the largest volume polymers in the world and is used tomake PET plastics (e.g., two liter PET bottles). It is also used to makepolyester fiber, which in turn is used to make clothes and other fabrics

In an embodiment, the aromatization catalyst may be used in theproduction of benzene which may be hydrogenated to form a hydrogenationproduct such as for example cyclohexane. For example, the benzene may behydrogenated in a process involving a high-purity benzene feed andpurified hydrogen. The conversion of benzene to cyclohexane isstoichiometric. A large portion of the cyclohexane production is used toproduce intermediates for nylons such as for example nylon 6 and nylon66. Nylon 6 is made by polymerizing caprolactam which is derived fromthe nitration of cyclohexane. Nylon 66 is made by polymerizing equalmolar quantities of adipic acid and hexamethylene diamine (HMDA). Adipicacid is made by a two-step air and nitric acid oxidation of cyclohexane.The adipic acid is converted to HMDA by the reduction of adiponitrile(an intermediate). Adipic acid produced from cyclohexane is also used tomanufacture esters for plasticizers and synthetic lubricants, as well asproduce polyeurethanes (synthetic leather).

In an embodiment, the aromatization catalyst functions to catalyze theproduction of benzene which may be further alkylated to produceethylbenzene which is a raw material for the production of styrene. Forexample, benzene may be combined, typically in molar excess, with asuitable alkylating reagent having from 2 to 54 carbon atoms such asolefins (e.g., ethylene, propylene), halogenated alkanes, or mixturesthereof. In one embodiment at least a portion of the benzene may bealkylated with ethylene to produce ethylbenzene; which may be optionallyfollowed by dehydrogenation of the ethylbenzene to styrene. In anotherembodiment at least a portion of the benzene may be alkylated withpropylene to produce cumene.

In an embodiment, an prolongated silica bound zeolite catalyst preparedas disclosed herein may have an increased zeolite:binder ratio, e.g.,greater than about 80:20 zeolite:binder, when compared to an otherwiseidentical silica bound zeolite catalyst lacking a prolongated silica asa binder. By having more zeolite and less binder, a catalyst support maybe prepared having an increased surface area for impregnation (e.g., Ptloading) and/or dispersion (e.g., Pt dispersion), thereby providing fora catalyst having higher levels of catalytically active materials thanan otherwise identical catalyst lacking a prolongated silica as abinder. Alternatively, an catalyst prepared as disclosed herein andhaving a traditional zeolite:binder ratio, e.g., equal to or less thanabout 80:20 zeolite:binder, may provide an catalyst with sufficientparticle strength suitable for use in a fluidized or moving catalystbed. For example, an catalyst comprising about 80:20 zeolite:prolongatedsilica may be sufficiently robust to withstand a continuous catalystregeneration process, in contrast to an otherwise identical catalystlacking a prolongated silica as a binder that is traditionally employedin a fixed catalyst bed to avoid damage to the catalyst.

The resulting prolongated silica bound zeolite catalyst may displayimprovements in catalytic performance consistent with the higher levelsof catalytically active materials. Improvements in catalytic performancemay be measured by any means known to one of ordinary skill in the art.When used as catalysts in an aromatization reaction, the catalyst ofthis disclosure may display a reduced Temperature at Start of Run(TSOR), a decreased fouling rate, higher liquid yield, an extendedcatalytic life, or combinations thereof. The prolongated silica boundzeolite catalysts may have a TSOR of from about 900° F. to about 937°F., alternatively of from about 907° F. to about 930° F., alternativelyof from about 910° F. to about 924° F. The prolongated silica boundzeolite catalysts of this disclosure may be further characterized by alifetime that is equal to or about 10% greater than an otherwiseidentical catalyst lacking a prolongated silica, alternatively equal toor about 20% greater, alternatively about 30% greater. Additionalmeasures of improved catalytic performance would be apparent to one ofordinary skill in the art.

EXAMPLES

The invention having been generally described, the following examplesare given as particular embodiments of the invention and to demonstratethe practice and advantages thereof. It is understood that the examplesare given by way of illustration and are not intended to limit thespecification of the claims to follow in any manner.

Example 1 Preparation of Prolongated Silica Bound KL-Zeolite

Support A was a prolongated silica bound KL-Zeolite containing about 88wt % KL-Zeolite. A mixture was prepared from about 671.9 grams (g) of Lzeolite and about 30 g of methyl cellulose. This mixture was thoroughlyblended in a muller before proceeding to the next step. To this mixture,about 400 g of an about 20 wt % aqueous solution of the prolongatedsilica (SNOWTEX®-UP, Nissan Chemical Industries) was added andthoroughly blended. To accomplish thorough blending the silica sol wasadded to the muller over an about 11 minute period. After the silica solwas added to the mixture, water was added to bring the moisture to alevel of about 35 wt % to about 40 wt % loss on ignition (LOI) forextrusion. Loss on ignition is the percentage of weight lost when asample is heated at about 1000° F. for about 1 hour in dry air. Themixture was then extruded through a 1/16 inch (1.6 mm) die. Theextrudates were then dried at about 250° F. (121° C.) for about 4 hours,followed by calcination for about 1 hour at about 932° F. (500° C.). Anabout 100 g portion of the calcined extrudate was then washed with about250 mL of about 100° F. (37.8° C.) deionized water. This wash time wassufficient to achieve good contacting of the solids and liquids. Thiswashing was repeated for a total of three washings. The washed extrudatewas then dried for about 4 hours at about 250° F. (121° C.) and thencalcined in air at about 900° F. (482° C.) for about 1 hour in flowingdry air.

Support B was a prolongated silica bound KL-Zeolite containing about 80wt % KL-Zeolite. This support was prepared according to the same methodas Support A with the exception that a about 30 wt % aqueous solution ofthe prolongated silica was used.

Support C was a spherical silica bound KL-Zeolite containing about 80 wt% KL-Zeolite. This support was prepared according to U.S. Pat. No.6,207,042 using Tosoh L-Zeolite, SI-350 Silica Sol, obtained from CCIC(Japan), and Methocel®, obtained from Dow Chemical Company, as anextrusion aid.

Example 2 Impregnation of Prepared Supports

Catalyst D comprised about 1 wt % Pt on prolongated silica boundKL-Zeolite containing about 88 wt % KL-Zeolite. The platinum-impregnatedKL-zeolite catalyst containing about 1.0 wt % platinum was prepared inthe following manner. An impregnating mixture of about 1.52 gtetraammineplatinum (II) chloride (TAPC), about 1.41 g ammonium fluoride(AF), about 0.64 g ammonium chloride (AC) and about 40.89 g water wasformed and added to a container containing about 80.17 g of theprolongated silica bound KL-zeolite extrudates of Support A usingincipient wetness techniques. The impregnated extrudates were thenallowed to stand for about 4 hours at room temperature. The impregnatedKL-zeolite was dried in a vacuum for about 3 hours at about 212° F. andthen calcined at about 585° F. for 1 hour in flowing dry air. Theresultant extrudates contained about 0.94 wt % Pt, about 0.95 wt % F,and about 0.67 wt % Cl as determined by standard analytical techniques.

Catalyst E comprised about 0.5 wt % Pt on prolongated silica boundKL-Zeolite containing about 88 wt % KL-Zeolite. The platinum-impregnatedKL-zeolite catalyst containing about 0.5 wt % platinum was preparedaccording to the method described for Catalyst D with the followingexceptions. The impregnating mixture instead contained about 0.75 gtetraammineplatinum (II) chloride (TAPC), about 1.45 g ammonium fluoride(AF), about 0.88 g ammonium chloride (AC) and about 40.89 g water. Theextrudate was formed and added to a container containing about 80.17 gof the prolongated silica bound KL-zeolite extrudates of Support A. Theresultant extrudates contained about 0.49 wt % Pt, 0.65 wt % F, andabout 0.48 wt % Cl by standard analytical techniques.

Catalyst F comprised about 1.0 wt % Pt on prolongated silica boundKL-Zeolite containing about 80 wt % KL-Zeolite. The platinum-impregnatedKL-zeolite catalyst containing about 1.0 wt % platinum was prepared inthe following manner. An impregnating mixture of about 1.52 gtetraammineplatinum (II) chloride monohydrate (TAPC), about 1.41 gammonium fluoride (AF), about 0.64 g ammonium chloride (AC) and about41.84 g water was formed and added to a container containing about 80.46g of the prolongated silica bound KL-zeolite extrudates of Support Busing incipient wetness techniques. The impregnated extrudates were thenallowed to stand for about 4 hours at room temperature. The impregnatedKL-zeolite was dried in a vacuum for about 3 hours at about 212° F.(100° C.) and then calcined at about 585° F. (307° C.) for about 1 hourin flowing dry air. The resultant extrudates contained about 0.97 wt %Pt, about 0.61 wt % F, and about 0.63 wt % Cl by standard analyticaltechniques.

Catalyst G about comprised about 1 wt % Pt on a spherical-silica boundKL-Zeolite containing about 80 wt % KL-Zeolite. A platinum-impregnatedKL-zeolite catalyst containing about 1.0 wt % platinum was preparedaccording to U.S. Pat. No. 6,207,042. The resultant extrudates containedabout 0.98 wt % Pt, about 0.68 wt % F, and about 0.82 wt % Cl bystandard analytical techniques.

Example 3 Catalyst Evaluations

Each of the extrudates from Example 2 were then ground and sieved toabout 20-40 mesh (0.84 mm-0.42 mm diameter) and placed in a reactorcomprising an about ¼ inch OD (6.4 mm) stainless steel reactor vessel ina temperature controlled furnace. The catalyst was dried and reducedunder flowing hydrogen without recycle at a temperature from roomtemperature to about 950° F. (510° C.). The reactor was then cooled toabout 930° F. (499° C.), and a feed stream of aliphatic hydrocarbons ata liquid hourly space velocity (LHSV) of about 12 hr⁻¹ and hydrogen atH₂:hydrocarbon mole ratio of about 1 was introduced to the reactorvessel at a feed rate of about 12 mL/min and a pressure of about 100psig. The reactor effluent composition was regularly analyzed by gaschromatography to indicate the weight percentage of total aromatics inthe C₅₊ fraction. The reactor temperature was then adjusted to achievethe desired total wt % aromatics in the C₅₊ product, typically about 70wt %, and performance data was then collected.

The catalysts prepared in accordance with Examples 1 and 2 belowillustrate effects of the prolongated silica morphology on the catalystefficiency. The results are summarized in Table 1.

TABLE 1 Impregnated Silica Zeolite:Binder Pt Fouling Rate C₅₊ SupportMorph. (Wt Ratio) (Wt %) TSOR ° F./hr (° C./hr) (Wt %) D Prolongated88:12 1 907° F. 0.14 92.4 (486° C.) (0.078) E Prolongated 88:12 0.5 937°F. 0.25 92.4 (503° C.) (0.14) F Prolongated 80:20 1 924° F. 0.18 93.1(501° C.) (0.10) G Spherical 80:20 1 931° F. 0.20 91.9 (comparison)(499° C.) (0.11)

The results in Table 1 demonstrate that the substitution of sphericalsilica with prolongated silica increased the zeolite:binder ratioresulting in a reduction in TSOR while producing comparable levels ofaromatics.

While various embodiments of the invention have been shown anddescribed, modifications thereof can be made by one skilled in the artwithout departing from the spirit and teachings of the invention. Theembodiments described herein are exemplary only, and are not intended tobe limiting. Many variations and modifications of the inventiondisclosed herein are possible and are within the scope of the invention.Where numerical ranges or limitations are expressly stated, such expressranges or limitations should be understood to include iterative rangesor limitations of like magnitude falling within the expressly statedranges or limitations (e.g., from about 1 to about 10 includes, 2, 3, 4,etc.; greater than 0.10 includes 0.11, 0.12, 0.13, etc.). Use of theterm “optionally” with respect to any element of a claim is intended tomean that the subject element is required, or alternatively, is notrequired. Both alternatives are intended to be within the scope of theclaim. Use of broader terms such as comprises, includes, having, etc.should be understood to provide support for narrower terms such asconsisting of, consisting essentially of, comprised substantially of,etc.

Accordingly, the scope of protection is not limited by the descriptionset out above but is only limited by the claims which follow, that scopeincluding all equivalents of the subject matter of the claims. Each andevery claim is incorporated into the specification as an embodiment ofthe present invention. Thus, the claims are a further description andare an addition to the embodiments of the present invention described inthe specification above. The discussion of a reference in the disclosureis not an admission that it is prior art to the present invention,especially any reference that may have a publication date after thepriority date of this application. The disclosures of all patents,patent applications, and publications cited herein are herebyincorporated by reference, to the extent that they provide exemplary,procedural or other details supplementary to those set forth herein.

1. A catalyst composition comprising a prolongated silica bound zeolitesupporting platinum and at least one halide, wherein the prolongatedsilica bound zeolite comprises a KL-zeolite and, wherein the catalystcomposition when employed in an aromatization process has a reducedtemperature at start of run when compared to an otherwise similarcatalyst composition lacking a prolongated silica bound zeolite.
 2. Thecomposition of claim 1 wherein the at least one halide comprises afluoride compound, a chloride compound or combinations thereof.
 3. Thecomposition of claim 1 wherein the prolongated silica has a diameter offrom about 5 nm to about 20 nm and a length of from about 30 nm to about400 nm.
 4. The composition of claim 1 wherein the platinum compoundcomprises ammonium tetrachloroplatinate, chloroplatinic acid,diammineplatinum (II) nitrite, bis-(ethylenediamine)platinum (II)chloride, platinum (II) acetylacetonate, dichlorodiammine platinum,platinum (II) chloride, tetraammineplatinum (II) hydroxide,tetraammineplatinum chloride, tetraammineplatinum (II) nitrate, orcombinations thereof.
 5. The composition of claim 1 wherein the platinumis present in an amount of from about 0.1 wt. % to about 5 wt. %.
 6. Acatalyst composition comprising a prolongated silica binder, aKL-zeolite, platinum metal and at least one halide wherein the ratio ofprolongated silica binder to KL-zeolite is equal to or greater thanabout 80:20 and the catalyst composition has a reduced temperature atstart of run when compared to an otherwise similar catalyst compositionlacking a prolongated silica binder.
 7. The composition of claim 6wherein the at least one halide comprises a fluoride compound, achloride compound or combinations thereof.
 8. The composition of claim 6wherein the platinum is present in an amount of from about 0.1 wt. % toabout 5 wt. %.
 9. The composition of claim 6 wherein the prolongatedsilica has a diameter of from about 5 nm to about 20 nm and a length offrom about 30 nm to about 400 nm.
 10. A process of making a prolongatedsilica bound zeolite catalyst comprising: a) mixing a zeolite, aprolongated silica, and water to form a mixture; b) shaping the mixtureinto a prolongated silica bound zeolite support; and c) adding one ormore catalytic compounds to the prolongated silica bound zeolite supportto form the prolongated silica bound zeolite catalyst, wherein thecatalytic compounds comprise a platinum compound and at least one halidecontaining compound, wherein the zeolite comprises KL-zeolite, andwherein the catalyst composition when employed in an aromatizationprocess has a reduced temperature at start of run when compared to anotherwise similar catalyst composition lacking a prolongated silicabound zeolite.
 11. The process of claim 10 wherein all or a portion ofthe water is provided in a prolongated silica sol.
 12. The process ofclaim 11 wherein the prolongated silica sol has a pH of from about 9.0to about 10.5 with a viscosity of equal to or less than about 20 mPa·sat 25° C. when provided in an aqueous solution of from about 20 to about30 vol %.
 13. The process of claim 10 wherein the mixture furthercomprises an extrusion aid.
 14. The process of claim 10 wherein step b)further comprises: extruding the mixture to form a green extrudate; anddrying the green extrudate to form a dried green extrudate; andcalcining the dried green extrudate to form the prolongated silica boundzeolite support, and wherein the adding one or more catalytic compoundsto the prolongated silica bound zeolite support to form the prolongatedsilica bound zeolite catalyst in step c) further comprises: contactingthe prolongated silica bound zeolite support with the platinum compoundand at least one halide-containing compound to form a metalized andhalided prolongated silica bound zeolite support; and drying andcalcining the metalized and halided prolongated silica bound zeolitesupport to form the prolongated silica bound zeolite catalyst.
 15. Theprocess of claim 10 wherein step b) further comprises: extruding themixture to form a green extrudate; drying the green extrudate to form adried green extrudate; calcining the dried green extrudate to form acalcined extruded base; washing the calcined extruded base to form awashed extruded base; drying the washed extruded base to form a driedextruded base; and calcining the dried extruded base to form theprolongated silica bound zeolite support, and wherein the adding one ormore catalytic compounds to the prolongated silica bound zeolite supportto form the prolongated silica bound zeolite catalyst in step c) furthercomprises: contacting the prolongated silica bound zeolite support withthe platinum compound and at least one halide-containing compound toform a metalized and halided prolongated silica bound zeolite support;and drying and calcining the metalized and halided prolongated silicabound zeolite support to form the prolongated silica bound zeolitecatalyst.
 16. The process of claim 13 wherein the extrusion aidcomprises comprise cellulose derivatives, ethylene glycol, stearic acidor combinations thereof.
 17. The process of claim 16 wherein thecellulose derivatives comprise a cellulose ether.